Colorimetric detection of melamine based on methanobactin-mediated synthesis of gold nanoparticles.

A simple and rapid field-portable colorimetric method for the detection of melamine in liquid milk was reported. Methanobactin (Mb) could reduce Au (III) to Au (0) and mediate the synthesis of gold nanoparticles (Au-NPs). Upon the addition of melamine, melamine interacted with oxazolone ring of Mb, which interrupted the formation of Au-NPs. Melamine could also stimulate the aggregation of formed Au-NPs. In this paper, these characteristics have been used to detect melamine in liquid milk by naked eyes observation with a detection limit of 5.56 × 10(-6)M (0.7 mg/kg). Further, the plasmon absorbance of the formed Au-NPs allowed the quantitative detection of melamine by UV-vis spectrometer. A linear correlation was existed between the absorbance and the melamine concentration ranging from 3.90 × 10(-7)M to 3.97 × 10(-6)M with a correlation coefficient of 0.9685. The detection limit (3σ) obtained by UV-vis spectrum was as low as 2.38 × 10(-7)M (i.e., 0.03 mg/kg).

Methanobactin-mediated one-step synthesis of gold nanoparticles.

Preparation of gold nanoparticles with a narrow size distribution has enormous importance in nanotechnology. Methanobactin (Mb) is a copper-binding small peptide that appears to function as an agent for copper sequestration and uptake in methanotrophs. Mb can also bind and catalytically reduce Au (III) to Au (0). In this study, we demonstrate a facile Mb-mediated one-step synthetic route to prepare monodispersed gold nanoparticles. Continuous reduction of Au (III) by Mb can be achieved by using hydroquinone as the reducing agent. The gold nanoparticles have been characterized by UV-visible spectroscopy. The formation and the surface plasmon resonance properties of the gold nanoparticles are highly dependent on the ratio of Au (III) to Mb in solution. X-ray photoelectron spectroscopy (XPS), fluorescence spectra and Fourier transform-infrared spectroscopy (FT-IR) spectra suggest that Mb molecules catalytically reduce Au (III) to Au (0) with the concomitant production of gold nanoparticles, and then, Mb statically adsorbed onto the surface of gold nanoparticles to form an Mb-gold nanoparticles assembly. This avoids secondary nucleation. The formed gold nanoparticles have been demonstrated to be monodispersed and uniform by transmission electron microscopy (TEM) images. Analysis of these particles shows an average size of 14.9 nm with a standard deviation of 1.1 nm. The gold nanoparticles are extremely stable and can resist aggregation, even after several months.